Entry | Seriesa | Initiator:Polymerb | Mwc | Mnb | Viscosityd | Flow Behaviore |
---|---|---|---|---|---|---|
w/w | kDa | kDa | Pa·s | |||
1 | I | 71:29 | 3.0 | 1.3 | 0.13 | Newtonian |
2 | I | 60:40 | 5.0 | 1.6 | 25 | Pseudoplastic |
3 | I | 41:59 | 6.1 | 2.3 | 81 | Pseudoplastic |
4 | I | 30:70 | 8.2 | 3.1 | 1.1 × 104 | Pseudoplastic |
5 | II | 80:20 | 2.7 | 1.2 | 1.2 | Newtonian |
6 | II | 68:32 | 3.1 | 1.4 | 1.6 | Newtonian |
7 | II | 56:44 | 3.8 | 1.7 | 2.8 | Newtonian |
8 | II | 44:56 | 4.4 | 2.1 | 7.4 | Newtonian |
9 | II | 23:77 | 7.2 | 4.0 | 63 | Newtonian |
10 | III | 92:8 | 1.9 | 1.0 | 0.92 | Newtonian |
11 | III | 69:31 | 2.6 | 2.3 | 2.8 | Newtonian |
12 | IV | 60:40 | 3.2 | 0.50 | 17 | Pseudoplastic |
13 | IV | 50:50 | 3.5 | 0.61 | 33 | Pseudoplastic |
14 | IV | 41:59 | 4.2 | 0.74 | 2.5 × 102 | Pseudoplastic |
15 | V | 46:54 | 3.2 | 0.65 | 3.0 | Newtonian |
16 | V | 24:76 | 5.8 | 1.3 | 35 | Newtonian |
17 | VI | 66:34 | 2.1 | 0.46 | 27 | Newtonian |
18 | VI | 56:44 | 2.2 | 0.53 | 5.7 | Newtonian |
19 | VI | 43:57 | 2.7 | 0.70 | 27 | Newtonian |
GPC, gel permeation chromatography; Mn, number average molecular weight; Mw, weight average molecular weight.
↵a Series number according to the data in Table 1.
↵b The relative amounts (w/w) of fatty acid initiator and polymer as well as the true polymer Mn values were calculated from relative 1H NMR peaks of either component.
↵c Mw was estimated by GPC relative to polystyrene standards and is reported in kilodaltons.
↵d Viscosity at shear rate 0.1 second−1.
↵e Flow behavior from shear rate 0.1–100 second−1.